激光刻痕对取向电工钢磁畴和铁损的影响

为了研究激光刻痕工艺参数对取向电工钢表面的磁畴形貌、刻痕线宽度和铁损的影响规律，开展了激光刻痕工艺试验。结果表明，激光刻痕后取向电工钢表面的磁畴宽度明显细化，且随着输入电流的增加，磁畴宽度先减小后增大；刻痕线宽度随着输入电流的增加而增大。对于本次试验样品，通过对比分析，确定最佳激光刻痕工艺参数为电流为 12 A，激光频率为 5 kHz，刻痕速度为 800 mm/s，该参数下铁损改善率可达 11.81%。     

The corrosion behavior and mechanism of X65 steel induced by iron‐oxidizing bacteria in the seawater environment

The corrosion behavior and mechanism of iron‐oxidizing bacteria (IOB) on X65 steel in seawater are studied. This study uses the methods of weight loss, electrochemical measurements, and surface analysis. The results show that the IOB increases the corrosion damage degree of steel. Pittings are observed in the medium with IOB. The potentiodynamic polarization curves show that the anodic reaction rate is accelerated in the corrosion process of IOB. The synergies in corrosion between the metal surface, abiotic corrosion products, and bacterial cells, and the pitting corrosion mechanism of X65 steel are discussed.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

镁对非调质钢中组织及硫化物的影响

摘要：为了探究不同镁含量对非调质钢中组织和硫化物形态、尺寸、分布及成分的影响，采用蔡司金相显微镜、扫描电子显微镜、小样电解等方法，分析了经高温电阻炉冶炼不同镁添加量的49MnVS3非调质钢。结果表明，由于镁蒸气压较高，在实验室冶炼中大量挥发，导致钢中镁的实际平均收得率仅为310%；镁的质量分数为0～22×10-6时，随着镁的质量分数的增加，钢中硫化物形态由Ⅱ类逐渐向Ⅰ类、Ⅲ类转变；钢中硫化物尺寸增大，硫化物的分布均匀性得到显著改善；钢中复合夹杂物比例明显增加，但MnS的比例出现下降；形成了细小弥散的氧化物，增加了奥氏体形核质点，具有细化组织的趋势。     

304不锈钢不同精炼渣碱度下夹杂物的演变

 为了提高304不锈钢的产品质量，结合生产实际，利用热力学计算和扫描电镜能谱分析方法, 研究了硅脱氧条件下，LF精炼渣碱度对304不锈钢在LF精炼、连铸过程夹杂物变化规律的影响。试验结果表明,随着冶炼过程进行，全氧质量分数和夹杂物数量依次减小。304不锈钢采用1.75高碱度炉渣，可以得到较低的全氧质量分数和夹杂物数量，但是夹杂物中Al2O3质量分数高，夹杂物熔点高。采用1.53低碱度炉渣，钢液中全氧质量分数较采用高碱度炉渣高，但是夹杂物中CaO、Al2O3质量分数相对较低，SiO2和MnO质量分数较高，夹杂物熔点低。针对304不锈钢产品可以采用不同的生产工艺路线来满足产品的不同需求。